Thermal mechanical and morphology characterization for epoxy/grafted marble and granite powder composites

Ali A.M.Yassene, S.Fares, A.Ashour,M.El-Ashry, M.K.Abo Assy, M.Abd El-Rahman


Direct radiation method has been used to graft styrene and acrylic acid monomer on to marble and granite powders. The grafted marble and granite powders were used as a filler of epoxy composites, they added to epoxy resin at weight percentage 20, 60 and 100 then cured at room temperature. The experimental results showed that the dispersion of marble powder in polymer matrix is remarkably improved, when the marble powder is grafted with monomers, the micro-hardness and impact strength of epoxy filled the modified marblewere higher than those of unmodified.When the epoxywas filled by unmodified and modified marble powder, its thermal stability was remarkably improved.


నిరాకరణ: ఈ సారాంశం ఆర్టిఫిషియల్ ఇంటెలిజెన్స్ టూల్స్ ఉపయోగించి అనువదించబడింది మరియు ఇంకా సమీక్షించబడలేదు లేదా నిర్ధారించబడలేదు

ఇండెక్స్ చేయబడింది

  • CASS
  • గూగుల్ స్కాలర్
  • J గేట్ తెరవండి
  • చైనా నేషనల్ నాలెడ్జ్ ఇన్‌ఫ్రాస్ట్రక్చర్ (CNKI)
  • CiteFactor
  • కాస్మోస్ IF
  • రీసెర్చ్ జర్నల్ ఇండెక్సింగ్ డైరెక్టరీ (DRJI)
  • రహస్య శోధన ఇంజిన్ ల్యాబ్‌లు
  • స్కాలర్ ఆర్టికల్ ఇంపాక్ట్ ఫ్యాక్టర్ (SAJI))
  • ICMJE

మరిన్ని చూడండి

జర్నల్ హెచ్-ఇండెక్స్

Flyer